Order Products : sales@su-jiao.com
Kepital® FV-30A
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g15kdu_KepitalFV30A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Anti-static grade with high flow |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 29 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.00 mm) | 2.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 63.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 25 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2580 | MPa | ISO 178 |
| Flexural Stress (23°C) | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 97.0 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Dielectric Strength | 19 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TROGAMID® TCR Film 100 µm | Evonik Industries AG | Nylon, Unspecified | TROGAMID® TCR Film |
| Nylene® 734 | Custom Resins Group | Nylon 6 | Nylene® |
| Hylac® GP29 | Ravago Manufacturing Americas, LLC | ABS | Hylac® |
| Sylvin 9915-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VALOX™ V2000DM resin | SABIC Innovative Plastics | PBT | VALOX™ |