Makrolon® SF800
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g0hm4g_Makrolon-SF800.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MVR (300 °C/1.2 kg) 5.0 cm³/10 min; structural foam; 5 % glass fiber reinforced; flame retardant; high viscosity; easy release; in combination with an appropriate blowing agent for the production of structural foam moldings |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density 1 | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage 2 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.55 | % | |
| Flow : 2.00 mm | 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 64.0 | MPa | |
| Break, 23°C | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 5.4 | % | |
| Break, 23°C | 40 | % | |
| Flexural Modulus 3(23°C) | 2900 | MPa | ISO 178 |
| Flexural Stress 4(23°C) | 100 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 5(23°C) | 6.2 | % | ISO 178 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | ISO 7391-PC,MFR,(,,)-05-9,GF5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -60°C, Complete Break | 150 | kJ/m² | |
| -30°C, Complete Break | 160 | kJ/m² | |
| 23°C, Complete Break | 220 | kJ/m² | |
| Notched Izod Impact Strength 6(23°C, Complete Break) | 12 | kJ/m² | ISO 7391 |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 25.0 | J | |
| 23°C | 30.0 | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
| -30°C | 4900 | N | |
| 23°C | 4400 | N |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 141 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 132 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 144 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 5.5E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 7.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 175 | V | |
| Solution B | 125 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 7(6.00 mm) | V-0 5VA | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 930 | °C | |
| 1.50 mm | 930 | °C | |
| 3.00 mm | 930 | °C | |
| Oxygen Index 8 | 36 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Pellets |
| 2 . | 60x60x2 mm, 500 bar |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2 mm/min |
| 6 . | Based on ISO 180-A, 3 mm |
| 7 . | Foamed; density in the foamed state: 900 to 1000 kg/m³ |
| 8 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 77-W002-B | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina MBU LILAC E 34/160-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ LX00486C compound | SABIC Innovative Plastics | PEEK | LNP™ STAT-KON™ |
| Plasmer 1080N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| LUVOCOM® 1105-9220 | LEHVOSS Group | PEEK | LUVOCOM® |