Order Products : sales@su-jiao.com
Bormed™ RD808CF
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Bormed™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g0UBfr_Bormed-RD808CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bormed RD808CF is a random copolymer with high ethylene content. This grade is suitable for the manufacturing of non-oriented cast films on chill roll process and blown films on tubular water quenching process as well as injection moulding and ISBM (2-stage process) for ampoules and bottles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molecular Weight Distribution | Narrow |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (23°C, Injection Molded) | 700 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | > 0.70 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm | 400 | MPa | |
| TD : 50 µm | 400 | MPa | |
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm | 30.0 | MPa | |
| TD : 50 µm | 30.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 540 | % | |
| TD : Break, 50 µm | 610 | % | |
| Instrumented Dart Impact (50 µm, Total Energy) | 30.0 | J | ISO 7765-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 140 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm) | > 140 | ASTM D2457 | |
| Haze (50.0 µm) | < 0.50 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3703C | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Manner Flexible PVC P8168 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TOTAL Polyethylene HDPE 2287 | TOTAL Refining & Chemicals | HDPE, HMW | TOTAL Polyethylene |
| DINALON® B1S25 M (Lubricated) | Grupo Repol | Nylon 6 | DINALON® |
| DINALON® PA 6.6 IGNÍFUGA | Grupo Repol | Nylon 66 | DINALON® |