TECHNYL® A 217-1 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g0H5ri_TECHNYLA2171NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 217-1 Natural is an unreinforced polyamide 66, heat stabilized, standard viscosity, for injection moulding. This grade offers all the primary properties of unreinforced polyamide 66. In addition it has improved resistance to high temperature and it can be used for components which have to withstand mid term temperature stresses. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183/A |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.3 | -- | % | ISO 62 |
| Saturated, 23°C | 8.3 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3200 | 1400 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield, 23°C | 85.0 | -- | MPa | ISO 527-2/1A |
| Fracture, 23°C | 55.0 | 50.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Yield, 23°C) | > 30 | > 300 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 3300 | -- | MPa | ASTM D790 |
| 23°C | 2900 | -- | MPa | ISO 178 |
| Flexural Strength | ||||
| 23°C | 115 | -- | MPa | ASTM D790 |
| 23°C | 120 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, not annealed | 233 | -- | °C | ASTM D648 |
| 0.45 MPa, not annealed | 200 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 75.0 | -- | °C | ASTM D648, ISO 75-2/Af |
| Melting Temperature | 262 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 265 - 275 | °C | |
| Middle Temperature | 270 - 280 | °C | |
| Front Temperature | 280 - 285 | °C | |
| Mold Temperature | 60 - 80 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For unfilled polyamide, Solvay recommends the use of high alloy steel with a weak chromium content. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2599 X 67122 | RTP Company | PC+ABS | RTP |
| RTP PP 20 GF NAT | RTP Company | PP, Unspecified | RTP |
| THERMOLAST® K TP6CDB (Series: EX) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Wondel® P PR0G4 | Nanjing Julong Engineering Plastics Co., LTD | PP, Unspecified | Wondel® P |
| LNP™ LUBRILOY™ R2000A compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |