Generic Polyester, TS - Glass Fiber
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fzSbpI_Generic-Polyester-TS---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Polyester, TS - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 - 2.02 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.069 - 0.36 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 - 0.35 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 48 - 91 | ASTM D785 | |
| Barcol Hardness | 29 - 58 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9560 - 43800 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 6.89 - 78.3 | MPa | ASTM D638 |
| 23°C | 31.6 - 114 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 0.50 - 1.3 | % | ASTM D638 |
| Flexural Modulus (23°C) | 6690 - 14700 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| 23°C | 75.8 - 178 | MPa | ASTM D790 |
| Yield, 23°C | 68.9 - 179 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 100 - 234 | MPa | ASTM D695 |
| Shear Strength (23°C) | 80.0 - 105 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 - 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 258 - 262 | °C | ASTM D648 |
| Continuous Use Temperature | 220 - 223 | °C | ASTM D794 |
| CLTE - Flow | 1.3E-5 - 2.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity (23°C) | 2.9E-4 - 0.27 | W/m/K | ASTM C177 |
| RTI Elec | 54.4 - 131 | °C | UL 746 |
| RTI | 54.4 - 164 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+7 - 1.8E+14 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.5E+6 - 2.2E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 2.0 - 20 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 0.0440 - 6.94 | ASTM D150 | |
| Dissipation Factor (23°C) | 3.0E-3 - 0.032 | ASTM D150 | |
| Arc Resistance | 179 - 190 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 500 - 606 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 22 - 47 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 151 - 152 | °C | |
| Mold Temperature | 152 - 173 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Polyester, TS - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULATEC® TinCo 50 | A. Schulman Europe | Nylon 6 | SCHULATEC® |
| TEKAFIN™ PB60G10 | Mando Advanced Materials Co., Ltd. | PP, Unspecified | TEKAFIN™ |
| THERMOLAST® K TC7TPZ (Series: GP/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Ferro PP NPP00GC20GY | Ferro Corporation | PP Homopolymer | Ferro PP |
| Sylvin 9604-95 Clear 896 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |