GAPEX® RPP30EB01HB BLACK
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fxz0GG_GAPEX-RPP30EB01HB-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GAPEX®RPP30EB01HB BLACK is a polypropylene homopolymer (PP Homopoly) material, which contains a 30% glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. GAPEX®The main characteristics of RPP30EB01HB BLACK are: chemical coupling. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | ASTM D955 |
| Transverse flow | 1.1 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 76.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.8 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 5620 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 119 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 75 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 0.339 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 149 | °C | ASTM D648 |
| Additional Information |
|---|
| Testing and measurements were performed at 73 +/-3°F and 50 +/-5% relative humidity unless otherwise noted. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 221 - 238 | °C | |
| Middle Temperature | 227 - 243 | °C | |
| Front Temperature | 232 - 260 | °C | |
| Nozzle Temperature | 232 - 260 | °C | |
| Processing (Melt) Temp | 221 - 238 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 5.08 - 12.7 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS PCA-3013 | Polymer Technology and Services, LLC | PC+PBT | PTS |
| Monprene® OM-16260-02 | Teknor Apex Company | TPE | Monprene® |
| Karina BLUE PVC COMPOUND 550-06/86-IS-SD (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina BLACK PVC COMPOUND 830-48/1 1-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Tribocomp® PA612 CF30 TS12 | Solvay Specialty Polymers | Nylon 612 | Tribocomp® |