OmniLon™ PA6 GBR30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniLon™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fxp6ma_OmniLon-PA6-GBR30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Fiber & Bead Reinforced, Nylon 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.10 to 0.40 | % | |
| Across Flow | 0.30 to 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 134 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 8270 | MPa | ASTM D790 |
| Flexural Strength | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 199 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 249 to 282 | °C | |
| Middle Temperature | 260 to 293 | °C | |
| Front Temperature | 260 to 293 | °C | |
| Nozzle Temperature | 260 to 293 | °C | |
| Processing (Melt) Temp | 260 to 293 | °C | |
| Mold Temperature | 26.7 to 82.2 | °C | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 218C V10 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Wellamid® GF1398-N1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| NOVALAST® 4001 | NOVA Polymers, Inc. | TPE | NOVALAST® |
| Chemical Resources GPPS300 | Chemical Resources, Inc. | PS (GPPS) | Chemical Resources |
| INEOS PP H02C-01 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |