Braskem PE HS4506
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fxDctl_BraskemPEHS4506.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HS4506 is a High Density Polyethylene specially developed for the manufacturing of blow molding fuel tanks. It has high molar mass and shows excellent processability. Besides, it shows excellent tenacity, high resistance to stress cracking, and outstanding impact resistance. Application: Mono and multilayer fuel tanks for automobiles; small volume automotive reservoirs; sheet extrusion for pickup rear protectors. Process: Blow Molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.945 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 5.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 2.00 mm, 100% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 24.0 | MPa | ASTM D638 |
| Fracture, molding | 38.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, molding | 11 | % | ASTM D638 |
| Fracture, molding | 1600 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 930 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 700 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 62.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 TFE 5 | RTP Company | Nylon 66 | RTP |
| RTP 2109 UP | RTP Company | PEI | RTP |
| Moplen HP648N | LyondellBasell Industries | PP Homopolymer | Moplen |
| Durethan® BKV 215 W1 902176 | LANXESS GmbH | Nylon 6 | Durethan® |
| Sylvin 8378-85 Yellow 4195 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |