Trithene® TS 7003
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Petroquimica Triunfo |
| Trademark: | Trithene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fwidau_Trithene-TS-7003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trithene®TS 7003 is a low density polyethylene material,. This product is available in Latin America and is processed by film extrusion. Trithene®The main features of TS 7003 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.27 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 11.0 | MPa | ASTM D638 |
| Fracture, molding | 17.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 590 | % | ASTM D638 |
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.15 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 5% secant, MD : 50 µm, blown film | 115 | MPa | ASTM D882 |
| 5% secant, TD : 50 µm, blown film | 125 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 27.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 23.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 300 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 630 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 190 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 300 | g | ASTM D1922 |
| TD : 50 µm, blown film | 230 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 50.0 µm, Blown Film) | 64 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 18 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 50 µm blown film produced on a 50 mm extruder, L/D=25, die gap=1.0 mm, BUR=2.3:1Melt Mass-Flow Rate, ASTM D1238, 190°C/2.16 kg: 0.23 to 0.30 g/10 minDensity, ASTM D1505: 0.922 to 0.924 g/cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 - 170 | °C | |
| Cylinder Zone 2 Temp. | 165 - 175 | °C | |
| Cylinder Zone 3 Temp. | 170 - 190 | °C | |
| Adapter Temperature | 185 - 200 | °C |
| Extrusion instructions |
|---|
| Recommended Blow Up Ratio: 2-3:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP111 | Southern Polymer, Inc. | PP Homopolymer | PRIMALENE |
| Sylvin 8675-65FU White 1357 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| HiFill® PA6/6 GF13 L YAG | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| ICORENE® N4420 | ICO Polymers EMEA, A Division of A. Schulman | PP Homopolymer | ICORENE® |
| Lusin® Lub PM 1001 | Chem-Trend L.P. | Unspecified | Lusin® |