Boda BDF331P
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Trademark: | Boda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fwdXfS_Boda-BDF331P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BDF331P is a low to medium viscosity curative incorporated fluoroelastomer copolymer. This grade is well suited for application where good tear resistance and excellent process properties are required. BDF331P can be compounded to meet the major fluoroelastomer specifications. BDF331P can be used for compression molding or injection molding of complex geometries. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 30 | MU | |
| Fluorine Content | 66 | % | |
| Solubility | LMW Ketones and esters |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MH 1(177°C) | 1.92 | N·m | |
| ML 2(177°C) | 0.160 | N·m | |
| t'90 3(177°C) | 2.5 | min | |
| ts2 4(177°C) | 1.1 | min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore A) | 76 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 6(Yield) | 13.5 | MPa | ASTM D412 |
| Tensile Elongation 7(Break) | 280 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 23 | % | ASTM D395B |
| Additional Information |
|---|
| Test Compound: Polymer: 100 MT Black (N990): 30 phr MgO: 3 phr Ca(OH)2: 6 phr Curing Condition: Press: 10 min at 170°C Oven: 24 hr at 230°C |
| Note Message | |
|---|---|
| 1 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 2 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 3 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 4 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 5 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 6 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 7 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa PET G20S | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PET | Zhongfa |
| Fainplast PVC CKL 93 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Ebalta MG 426 / Comp. A+B | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| Petrotene® PP A3 C40 NTLA010 PH309 | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |
| Techsil® RTV27905 | Techsil Limited | Silicone Rubber, RTV-2 | Techsil® |