| Diakon®CLH952L is a polymethyl methacrylate-acrylic material,. This product is available in Europe and is processed by extrusion or injection molding. Diakon®The main characteristics of the CLH952L are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 1.7 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.70 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 92 | ISO 2039-2 | |
| Ball Indentation Hardness (H 961/30) | 180 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 83.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 3200 | MPa | ISO 178 |
| Flexural Stress | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 1.9 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 101 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 109 | °C | ISO 306/A |
| -- | 103 | °C | ISO 306/B |
| CLTE - Flow | 7.1E-5 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Flammability Index | 650 | °C | IEC 60695-2-12 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ISO 489 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| Haze | 0.40 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Hopper Temperature | 50.0 - 90.0 | °C | |
| Rear Temperature | 200 - 240 | °C | |
| Middle Temperature | 210 - 260 | °C | |
| Front Temperature | 210 - 270 | °C | |
| Nozzle Temperature | 220 - 260 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Hopper Temperature | 50.0 - 80.0 | °C | |
| Cylinder Zone 1 Temp. | 160 - 240 | °C | |
| Cylinder Zone 2 Temp. | 180 - 250 | °C | |
| Cylinder Zone 3 Temp. | 200 - 250 | °C | |
| Cylinder Zone 4 Temp. | 220 - 260 | °C | |
| Adapter Temperature | 210 - 270 | °C | |
| Die Temperature | 210 - 270 | °C |
| Extrusion instructions |
|---|
| Vent Zone Temperature: 220-270°CZone 6 Temperature: 220-270°CZone 7 Temperature: 210-270°CZone 8 Temperature: 210-270°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOND 2001 | SILON s.ro | EVA | TABOND |
| Expandable PS F32MB | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| HAIPLEN EP50 TC4 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Kepital® F10-01 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| LNP™ LUBRICOMP™ RFL36XXY compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |