IROGRAN® A 85 D 5001 DP
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fvfEKP_IROGRAN-A-85-D-5001-DP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 85 D 5001 DP is a antistatic, polyester based thermoplastic polyurethane intended for extrusion applications and injection moulding. IROGRAN A 85 D 5001 DP is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable in flat die, cast die extrusion processes. IROGRAN A 85 D 5001 DP is a development material. PERFORMANCE FEATURES
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.19 | g/cm³ | ASTM D792, DIN 53479 |
| Melt Volume-Flow Rate (MVR) (190°C/21.6 kg) | 75.0 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, DIN 53505 | ||
| Shore A, Injection Molded | 85 | ||
| Shore D, Injection Molded | 34 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | |||
| -- | 25 | mm³ | DIN 53516 |
| -- | 25 | mm³ | ASTM D395 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | |||
| 100% Strain | 5.58 | MPa | ASTM D412 |
| 100% Strain | 5.00 | MPa | DIN 53504 |
| 300% Strain | 5.58 | MPa | ASTM D412 |
| 300% Strain | 11.0 | MPa | DIN 53504 |
| Tensile Strength 4(Break) | 40.0 | MPa | ASTM D412, DIN 53504 |
| Tensile Elongation 5 | |||
| Break | 830 | % | ASTM D412 |
| Break | 620 | % | DIN 53504 |
| Tear Strength 6 | |||
| -- | 105 | kN/m | ASTM D624 |
| -- | 70 | kN/m | ISO 34-1 |
| Bayshore Resilience 7 | 36 | % | ASTM D2632 |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Surface Resistivity | 1.0E+8 | ohms |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Hot Air Dryer | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| Hopper Temperature | 25.0 to 45.0 | °C | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 190 to 210 | °C | |
| Nozzle Temperature | 185 to 210 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 180 to 205 | °C | |
| Cylinder Zone 2 Temp. | 180 to 205 | °C | |
| Cylinder Zone 3 Temp. | 180 to 205 | °C | |
| Cylinder Zone 4 Temp. | 180 to 205 | °C | |
| Cylinder Zone 5 Temp. | 180 to 205 | °C | |
| Adapter Temperature | 180 to 205 | °C | |
| Die Temperature | 185 to 205 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Injection Molded |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| 7 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 0.5.NB | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |
| Manner Flexible PVC X3412 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TOTAL Polypropylene PPH 9020 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Garaflex™ X 97-234-D NAT | AlphaGary | PVC Alloy | Garaflex™ |
| PEXLOY™ PXP-413UV-BK10 | Pier One Polymers, Inc. | PC+Polyester | PEXLOY™ |