UBESTA 3030 JLX2
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | UBE Engineering Plastics, S.A. |
| Trademark: | UBESTA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fuVZUQ_UBESTA-3030-JLX2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UBESTA 3030 JLX2 is semiplasticized and UV-stabilized Polyamide 12 most suitable for smooth and corrugated fuel lines. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.4 | % | ISO 294-4 |
| Flow direction | 0.80 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 76 | ISO 2039-2 | |
| Durometer Hardness (Shore D) | 74 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 17 | % | ISO 527-2 |
| Fracture | 200 | % | ISO 527-2 |
| Flexural Modulus | 600 | MPa | ISO 178 |
| Flexural Stress | 26.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, complete fracture | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C, complete fracture | 40 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 98.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 176 | °C | ISO 3146 |
| CLTE - Flow | 1.6E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Tensile Strain at Break, ISO 527: >200%Abrasion Loss, ISO 9352, CS-17, 1000 rev.: 7 mg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PC 63 T 25 | Plastcom | PP, Unspecified | SLOVALEN® |
| Stylac™ A100 | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| ExxonMobil™ PP9574E6 | ExxonMobil Chemical | PP Random Copolymer | ExxonMobil™ |
| Geon™ Vinyl Flexible XV3782 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Geon™ Vinyl Flexible R1480E | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |