RTP EMI 1061 HF
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fuNfA9_RTPEMI1061HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stainless Steel Fiber - EMI/RFI Shielding - Electrically Conductive - High Flow |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.2 - 1.6 | % | ASTM D955 |
| Moisture Content | 0.030 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay | sec | FTMS 101C 4046.1 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 | MPa | ASTM D638 |
| Tensile Strength | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 51.7 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | < 1.0E+3 | ohms | ESD STM11.11 |
| -- | < 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity | < 10 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -29 | °C | |
| Processing (Melt) Temp | 193 - 221 | °C | |
| Mold Temperature | 63 - 82 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps.Remove hopper magnets.Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIGITRON 10001 | Ovation Polymers Inc. | PC | RIGITRON |
| RTP 1001 GB 15 TFE 5 | RTP Company | PBT | RTP |
| SCHULAMID® 6 HV 2 FR | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Versaflex™ HC MT222 | PolyOne Corporation | TPE | Versaflex™ |
| NEXT SIGNATURE PPH G30-300 | NEXT Specialty Resins, Inc. | PP Homopolymer | NEXT SIGNATURE |