TPX® DX310
| Category: | PMP Copolymer , Polymethylpentene Copolymer |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | TPX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fsWg8a_TPX-DX310.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TPX® DX310 is a Polymethylpentene Copolymer (PMP Copolymer) material. It is available in North America for extrusion coating or fiber (spinning) extrusion. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.833 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 100 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 42 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 820 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 20.0 | MPa | |
| Break, 23°C | 10.0 | MPa | |
| Tensile Elongation (Break, 23°C) | 40 | % | ASTM D638 |
| Flexural Modulus (23°C) | 630 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 21.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 25 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 130 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 147 | °C | ASTM D1525 |
| Melting Temperature | 223 | °C | DSC |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 65 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.10 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.460 | ASTM D542 | |
| Transmittance | 93.0 | % | ASTM D1003 |
| Haze | 2.1 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHLEN ST920 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| AKROMID® B3 GK 30 1 L black (4674) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| Caltex PP M570 | GS Caltex | PP Impact Copolymer | Caltex PP |
| Jam 22502AA | Jam Petrochemical Company | LLDPE | Jam |
| Sylvin 5150-90 Yellow 4124 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |