Infino NE-1030TV
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fpy8iQ_InfinoNE1030TV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Infino NE-1030TV is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical/electronic applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 75 | g/10 min | ASTM D1238, ISO 1133 |
| 250°C/2.16 kg | 27 | g/10 min | ASTM D1238 |
| 250°C/2.16 kg | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.060 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.060 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.060 | % | ISO 2577 |
| Traffic : 3.20mm | 0.060 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 116 | ASTM D785 | |
| R scale | 116 | ISO 2039-2 | |
| Pencil Hardness 1 | 2B | JIS K5401 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2200 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 3 | 61.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Fracture 4 | 59.0 | MPa | ASTM D638 |
| Fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 5 | 60 | % | ASTM D638 |
| Fracture | 60 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 6 | 2500 | MPa | ASTM D790 |
| -- 7 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 8 | 86.0 | MPa | ASTM D790 |
| -- 9 | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10(23°C) | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 440 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 170 | J/m | ASTM D256 |
| 23°C 11 | 25 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm | 66.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 84.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 68.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 87.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-0 | UL 94 | |
| 3.0 mm | V-0 | UL 94 | |
| 2.5 mm | 5VB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 500g |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 50 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.8 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | Thickness: 4mm |
| 11 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 6455 | Covestro - Polycarbonates | PC | Makrolon® |
| PPR PPCO06 | Premier Plastic Resins, Inc. | PP Copolymer | PPR |
| SABIC® PP QR674K | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® PP |
| Evermore PUR B-637ND | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| POTICON OA10 | Otsuka Chemical Co., Ltd. | Acetal (POM) Copolymer | POTICON |