Razamid® A121 GR30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Razin™ Engineering Plastics |
| Trademark: | Razamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fptgk3_Razamid-A121-GR30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Razamid A121 GR30 is an injection grade black color polyamide 66 resin reinforced with 30% Glass Fiber. It combines good strength, stiffness and toughness as well as excellent heat, chemical and abrasion resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 195 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 9100 | MPa | ASTM D790 |
| Flexural Strength | 290 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 15 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 257 | °C | |
| 1.8 MPa, Unannealed | 255 | °C | |
| Vicat Softening Temperature | 240 | °C | ASTM D1525 |
| Peak Melting Temperature | 260 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 265 to 300 | °C | |
| Front Temperature | 275 to 305 | °C | |
| Processing (Melt) Temp | 275 to 310 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 55.0 to 140 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L AB605C | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Copolymer | POLYPRO® |
| Quadrathane™ ARC-90A | Biomerics, LLC | TPU-PC | Quadrathane™ |
| Fainplast PVC CKL 80/E | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Fiberfil® PP-61/VO | Fiberfil® Engineered Plastics Inc. | PP Copolymer | Fiberfil® |
| OLEFISTA™ QU1549A | Mitsubishi Chemical Performance Polymers, Inc. | Elastomer, Specialty | OLEFISTA™ |