LNP™ THERMOCOMP™ KF004 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fplp99_LNPTHERMOCOMPKF004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP KF004 is a compound based on Acetal Copolymer containing Glass Fiber. Added features include : Chemically Coupled. Also known as: LNP* THERMOCOMP* Compound KFX1004 Product reorder name: KF004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.54 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.50 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 104 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 5500 | MPa | ISO 178 |
| Flexural Stress | 122 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 157 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 6.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2205 LF | RTP Company | PEEK | RTP |
| Mirakutoran® TPU E795PNAT | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Wellamid® GS25-66 22LH-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Multi-Pro® 0405 KU | Multibase, A Dow Corning Company | PP, Unspecified | Multi-Pro® |
| Pujie CPE-3611 | Zhanhua Pujie Chemical Technology Co.,Ltd | CPE | Pujie |