NEMCON H PC DP184
| Category: | PC , Polycarbonate |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | NEMCON H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fpBkmc_NEMCON-H-PC-DP184.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermally conductive Polycarbonate |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 7810 | MPa | ASTM D638 |
| Tensile Strength 2(Break, 23°C) | 55.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C) | 2.0 | % | ASTM D638 |
| Flexural Modulus 4(23°C, 50.0 mm Span) | 6750 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 23°C, 50.0 mm Span) | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Conductivity | Internal Method | ||
| 23°C 6 | 0.50 to 1.0 | W/m/K | |
| 23°C 7 | 5.0 to 8.0 | W/m/K |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 250 to 260 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 265 to 280 | °C | |
| Mold Temperature | 90.0 to 125 | °C | |
| Back Pressure | 0.276 to 0.552 | MPa | |
| Screw Speed | 60 to 120 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Through Plane |
| 7 . | In Plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELNEX™ RMG02 | Japan Polychem Corporation | PP Random Copolymer | WELNEX™ |
| ADDILENE PMD 50213 | ADDIPLAST | PP Copolymer | ADDILENE |
| Flexalloy® 9750-80 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| DuraFlex 202-6 | Evermore Chemical Industry Co., Ltd. | TPU-Polyether | DuraFlex |
| Karina WHITE PVC COMPOUND BT-0002/17 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |