Witcom PA66 2010/100 Blue
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fp9xYt_Witcom-PA66-2010-100-Blue.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Soft magnetic, metal and X-ray detectable |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.71 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.90 - 1.3 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 3.4 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | < 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 - 10 | % | ISO 527-2 |
| Flexural Modulus | 3500 | MPa | ISO 178 |
| Flexural Stress | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 40 | kJ/m² | ISO 180/1U |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | ISO 1210 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 275 - 295 | °C | |
| Mold Temperature | 60.0 - 95.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 1.00 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 - 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 660.75 | RTP Company | ABS | RTP |
| Vibrathane® 6020 | Chemtura | PUR-Ester/MDI | Vibrathane® |
| TRANSMARE® 14CT60-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| LNP™ STAT-KON™ EE004 compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |
| LNP™ THERMOCOMP™ RF00CSXS compound | SABIC Innovative Plastics Asia Pacific | Nylon 66 | LNP™ THERMOCOMP™ |