AKROMID® A3 GF 30 1 L black (4436)
| Category: | Nylon 66+PP , Polyamide 66 + PP |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fp5ccY_AKROMID-A3-GF-30-1-L-black-4436-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GF 30 1 L black (4436) is a 30% glass fibre reinforced and heat stabilised polyamide-blend with a reduced density compared to standard PA6.6 GF 30 Applications are mainly technical components in the automotive and electronic industry, where a weight and cost reduction is required |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.26 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 10.0 | -- | cm³/10min | ISO 1133 |
| Spiral Flow | 101 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.70 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.2 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8400 | 6700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 150 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | 4.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8200 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 220 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 13 | -- | kJ/m² | |
| 23°C | 15 | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 73 | -- | kJ/m² | |
| 23°C | 77 | 70 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 246 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 150 | -- | °C | ISO 75-2/C |
| Melting Temperature 3 | 262 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.800 mm) | 675 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ E 08/88 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| UNIGARD™ RE DFDA-1980 NT | The Dow Chemical Company | TP, Unspecified | UNIGARD™ |
| Gallonprene® GP420-7503 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Formolon® 38 | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| OTECH PVC OE7444 - Gasket | OTECH Corporation | PVC, Unspecified | OTECH PVC |