Rilsan® BUM 30 O
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | follCl_Rilsan-BUM-30-O.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® BUM 30 O is a glass bead reinforced polyamide 11 produced from a renewable source. The incorporation of glass beads yields a virtually isotropic reinforced product. This natural grade dedicated to injection is specially designed for drinking water application: WRAS (UK). MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (235°C/5.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 77 | ||
| Shore D, 15 sec | 71 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1850 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 31.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 40 | % | ISO 527-2 |
| Flexural Modulus | 1600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 96 | kJ/m² | |
| 23°C | 96 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 189 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA11, MR, 18-020, GB 30 | ISO 1874 | |
| Renewable Carbon Conent | > 97 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 40.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vistalon™ 3666 | ExxonMobil Chemical | EPDM | Vistalon™ |
| Kepex® 3725M7 | Korea Engineering Plastics Co., Ltd | PBT+PET | Kepex® |
| KOPA® KN333HFBL | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Isocor™ 6105 | Shakespeare Monofilaments and Specialty Polymers | Nylon 610 | Isocor™ |
| Sylvin 9077-85C Yellow 449 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |