| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latigloss |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | foQygE_Latigloss-66-H2-G-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 66 (PA 66). Heat stabilised. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.65 to 0.90 | % | |
| Flow : 2.00 mm | 0.30 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 16000 | MPa | |
| 60°C | 14000 | MPa | |
| 90°C | 8000 | MPa | |
| 120°C | 5000 | MPa | |
| 150°C | 3800 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 220 | MPa | |
| Break, 60°C | 160 | MPa | |
| Break, 90°C | 110 | MPa | |
| Break, 120°C | 85.0 | MPa | |
| Break, 150°C | 70.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.5 | % | |
| Break, 60°C | 4.0 | % | |
| Break, 90°C | 8.0 | % | |
| Break, 120°C | 10 | % | |
| Break, 150°C | 11 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 85 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 140 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 235 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 130 | °C | |
| Vicat Softening Temperature | 250 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 7.0E-6 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC3GPN (Series: GP/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| NEXUS ABS ABSGF30 | Nexus Resin Group, LLC. | ABS | NEXUS ABS |
| Axiall PVC HF-6597 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Hax™ HFC 0108 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| LNP™ LUBRICOMP™ DBL349E compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |