Plavis® N
| Category: | PI, TP , Thermoplastic Polyimide |
| Manufacturer: | Comco Nylon GmbH |
| Trademark: | Plavis® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | foGpNo_PlavisN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PLAVIS is a super engineering plastic. PLAVIS polyimide has a unique chemical structure with some of the highest properties availiable. Nitrogen bonded to 3 carbons is the critical part of the chain and imparts the plastic with remarkable features and benefits. DAELIM makes PLAVIS isostatic molded rods have uniform properties in all directions. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Water Absorption 1(24 hr, 50%RH) | 0.90 - 1.1 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, Compression Molded) | 90 - 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D1708 | ||
| Fracture, 23°C | 88.3 | MPa | ASTM D1708 |
| Fracture, 260°C | 41.2 | MPa | ASTM D1708 |
| Tensile Elongation 3 | ASTM D1708 | ||
| Fracture, 23°C | 8.0 | % | ASTM D1708 |
| Fracture, 260°C | 6.0 | % | ASTM D1708 |
| Flexural Modulus | ASTM D790 | ||
| 23°C, molded | 3040 | MPa | ASTM D790 |
| 260°C, molding | 1670 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| 23°C, molded | 113 | MPa | ASTM D790 |
| 260°C, molding | 58.8 | MPa | ASTM D790 |
| Compressive Modulus 4 | 2350 | MPa | ASTM D695 |
| Compressive Strength 5 | ASTM D695 | ||
| 1% strain, 23°C | 24.5 | MPa | ASTM D695 |
| 10% strain, 23°C | 128 | MPa | ASTM D695 |
| Coefficient of Friction 6 | 0.32 | ||
| Wear Rate | 33 | mm/sec |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow 7(23 to 260°C) | 5.5E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity 8(25°C) | 0.36 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 9 | 1.0E+14 - 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity 10(23°C) | 1.0E+16 - 1.0E+18 | ohms·cm | ASTM D257 |
| Dielectric Strength 11 | 22 | kV/mm | ASTM D149 |
| Dielectric Constant 12(23°C, 1 MHz) | 3.75 | ASTM D150 |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | Compression Molded |
| 3 . | Compression Molded |
| 4 . | Compression Molded |
| 5 . | Compression Molded |
| 6 . | Compression Molded |
| 7 . | Compression Molded |
| 8 . | Compression Molded |
| 9 . | Compression Molded |
| 10 . | Compression Molded |
| 11 . | Compression Molded |
| 12 . | Compression Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EVALENE® PP PRB0201 | JG Summit Petrochemical Corporation | PP Random Copolymer | EVALENE® PP |
| Latamid 66 H2 G/35-V0KB | LATI S.p.A. | Nylon 66 | Latamid |
| LNP™ THERMOCOMP™ WZ002 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |
| LNP™ THERMOCOMP™ RF008ESZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Daelim Po1y® XP9400S | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |