Tenac™-C MT754
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™-C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | foG22K_Tenac--C-MT754.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™-C MT754 is an Acetal (POM) Copolymer product filled with mineral. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™-C MT754 include engineering/industrial parts and housings. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.0 to 1.2 | % | Internal Method |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4800 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Break | 61.0 | MPa | ISO 527-2 |
| -- | 60.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break | 7.0 | % | ASTM D638 |
| Break | 5.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5000 | MPa | ASTM D790 |
| -- | 4800 | MPa | ISO 178 |
| Flexural Strength | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 163 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 161 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 150 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 131 | °C | ISO 75-2/A |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mowiol® 28-99 LA | Kuraray Co., Ltd. | PVOH | Mowiol® |
| KumhoSunny AES HW602HF | Shanghai KumhoSunny Plastics Co., Ltd. | AES | KumhoSunny AES |
| INEOS PP 101-XA12 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| Karina CLEAR PVC COMPOUND -E 75/2001-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polimid B 34 | Poliblend S.p.a. | Nylon 6 | Polimid B |