Eltex® TUB 433-NA00

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	Eltex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	fnDd8b_Eltex-TUB-433-NA00.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Eltex TUB 433-NA00 is a low melt flow rate, long term heat stabilized, high impact copolymer for pipe, blow moulding and sheet extrusion applications. It offers a very good balance stiffness - impact strength (even at low temperature) and excellent processability.

Applications:

Non-pressure pipes / fittings

Blow moulding

Sheet extrusion

Benefits and Features:

High impact resistance

Good rigidity

Excellent melt strength

Long term heat stability

Excellent processability (for solid and structured wall pipes extrusion)

General Information
Additive	Heat Stabilizer
Features	Good Melt Strength Good Processability Good Stiffness Good Thermal Stability Heat Stabilized High Impact Resistance Impact Copolymer Low Flow Low Temperature Impact Resistance Medium Rigidity
Uses	Blow Molding Applications Fittings Piping Sheet
RoHS Compliance	Contact Manufacturer
Processing Method	Blow Molding Extrusion Pipe Extrusion Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	0.30	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus ¹	1500	MPa
Tensile Stress (Yield, 23°C, 4.00 mm, Injection Molded)	28.0	MPa	ISO 527-2/50
Tensile Strain (Yield, 23°C, 4.00 mm, Injection Molded)	9.0	%	ISO 527-2/50
Flexural Modulus ²(23°C, 4.00 mm, Compression Molded)	1500	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength ³			ISO 179/1eA
-20°C, Injection Molded	7.0	kJ/m²
0°C, Injection Molded	18	kJ/m²
23°C, Injection Molded	> 50	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	95.0	°C	ISO 75-2/B
Vicat Softening Temperature	155	°C	ISO 306/A
Melting Temperature	165	°C	ASTM D3417
Oxidation Induction Time (200°C)	> 30	min	DIN EN 728

Note Message
1 .	Calculated from ring stiffness measurements carried out on 110 mm solid wall pipes
2 .	Cooling Rate = -15°C/min
3 .	4 mm thickness

Resin Grade	Manufacturer	Category	Trademark
RTP 1307 TFE 15	RTP Company	PPS	RTP
DOW™ LDPE 757A	The Dow Chemical Company	LDPE	DOW™ LDPE
ACCUCOMP™ ACE091L	ACLO Compounders Inc.	Acetal (POM) Copolymer	ACCUCOMP™
Plexiglas® 7H	Evonik Industries AG	Acrylic (PMMA)	Plexiglas®
LNP™ THERMOCOMP™ JF006E compound	SABIC Innovative Plastics	PESU	LNP™ THERMOCOMP™