Taitalac® 1003
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Taita Chemical Company, Ltd. |
| Trademark: | Taitalac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fkOfEt_Taitalac-1003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Taitalac®1003 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America or Asia Pacific region. The processing method is extrusion or injection molding. Taitalac®The main features of the 1003 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 3.5 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 35 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | < 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | < 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, 23°C, 3.18mm | 36.5 | MPa | ASTM D638 |
| Fracture, 23°C, 3.18mm | 32.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.18 mm) | 40 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | 2480 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 23°C) | 66.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.18 mm | 230 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 84.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 98.0 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 - 210 | °C | |
| Middle Temperature | 190 - 220 | °C | |
| Front Temperature | 180 - 210 | °C | |
| Nozzle Temperature | 200 - 230 | °C | |
| Processing (Melt) Temp | 170 - 180 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.345 - 0.483 | MPa | |
| Screw Speed | 30 - 100 | rpm |
| Injection instructions |
|---|
| Injection Pressure: Low to Moderate |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 30 HI K1871 | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Sasol Polymers PP CPV340 | Sasol Polymers | PP Impact Copolymer | Sasol Polymers PP |
| Sylvin 9993-65 Yellow 4141 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Karina IVORY PVC COMPOUND -E 807D35/ 1-C-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9657-85 Clear Green 3178 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |