DENKA Polymer Alloy HS-G193
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA Polymer Alloy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fk14BU_DENKA-Polymer-Alloy-HS-G193.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DENKA Polymer Alloy HS-G193 is a Polycarbonate + ABS (PC+ABS) product. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 | g/cm³ | ASTM D792 |
| 23°C | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.50 to 0.70 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 120 | ASTM D785 | |
| R-Scale | 121 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 56.0 | MPa | ASTM D638 |
| -- | 2460 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 62.0 | MPa | |
| Break | 48.0 | MPa | |
| Nominal Tensile Strain at Break | 60 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2550 | MPa | ASTM D790 |
| -- 3 | 2550 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 88.0 | MPa | ASTM D790 |
| -- 5 | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 75 | kJ/m² | ISO 179 |
| Notched Izod Impact | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed 6 | 105 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 99.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 115 | °C | ISO 306/B, ASTM D1525 7 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure | 0.490 to 1.47 | MPa |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 15 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 15 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Edgewise |
| 7 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PA66 6G/3L1 | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| CGPC PVC SO-30X (70 phr Plasticizer C) | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| EVERLON® TP-40D | Ever Polymer Co., Ltd. | SEBS | EVERLON® |
| KRATON® D1163 P | Kraton Polymers LLC | SIS | KRATON® |
| Hostacom HKC 431N D72643 | LyondellBasell Industries | PP Homopolymer | Hostacom |