Toyolac® 100-322
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fiY0sf_Toyolac-100-322-79363.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® 100-322 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| 23°C | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 113 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 49.0 | MPa | ASTM D638 |
| 23°C | 54.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 48 | % | ASTM D638 |
| Break, 23°C | 13 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2300 | MPa | ASTM D790 |
| 23°C | 2350 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 74.0 | MPa | ASTM D790 |
| 23°C | 78.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 140 | J/m | |
| -30°C, 12.7 mm | 120 | J/m | |
| 0°C, 3.20 mm | 200 | J/m | |
| 0°C, 12.7 mm | 180 | J/m | |
| 23°C, 3.20 mm | 270 | J/m | |
| 23°C, 12.7 mm | 230 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 87.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 83.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | |
| CLTE - Flow | 7.4E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer SG5 | Shanghai Potomer International Trade Co., Ltd. | PVC, Rigid | Shanghai Potomer |
| Vinnolit® PA 5470/5 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| Badaflex® TPE-S 75A 1205 2K S2 | Bada AG | SEBS | Badaflex® |
| Epoxies, Ect. 20-3035 (Cat.140) | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Iupilon® HL-3003 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |