Safrene® M 5010PE 100
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Safripol (PTY) LTD |
| Trademark: | Safrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fhv2h0_Safrene-M-5010PE-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HDPE M 5010PE 100 Polyethylene Resin is a high molecular mass grade with good impact strength, abrasion, chemical and UV resistance, complying with the PE100 (MRS 10) requirements of ISO 4427. HDPE M 5010PE 100 Polyethylene Resin is suitable for all dimensions of PE 100 piping where transportation of potable water, irrigation, effluent, slurry and certain chemical substances is required. HDPE M 5010PE 100 Polyethylene Resin is supplied only in special UV resistant black granular form. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.958 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 9.0 | g/10 min | |
| 190°C/5.0 kg | 0.25 | g/10 min | |
| Viscosity Number (Reduced Viscosity) | 390.0 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, Compression Molded | 24.0 | MPa | |
| Break, Compression Molded | 35.0 | MPa | |
| Tensile Strain (Break, Compression Molded) | > 600 | % | ISO 527-2/50 |
| Flexural Stress (3.5% Strain, Compression Molded) | 19.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C, Compression Molded | 6.0 | kJ/m² | |
| 23°C, Compression Molded | 20 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 67.0 | °C | ISO 306/B |
| Peak Crystallization Temperature (DSC) | 130 to 133 | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Unannealed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2809-80 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| APEX® 832-NL | Teknor Apex Company | PVC, Flexible | APEX® |
| Diakon® TD625 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Edgetek™ PC-15CF-15GF/000 NH FR V0 Black | PolyOne Corporation | PC | Edgetek™ |
| Mafill® CR H 8044 P060 | Ravago Group | PP Homopolymer | Mafill® |