VESTODUR® HI19

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	Evonik Industries AG
Trademark:	VESTODUR®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	fhU8Zg_VESTODUR-HI19.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Evonik manufactures a range of polybutylene terephthalate compounds that are supplied under the registered trademark VESTODUR®. Material properties characterizing VESTODUR® compounds are:

high thermostability

high stiffness

low water absorption resulting in high dimensional stability

high hardness

good strength

good sliding friction behavior, low abrasion

good creep behavior

good electrical properties

good chemical resistance

good weathering resistance

good processability

no tendency to form stress cracks

General Information
Features	Good Abrasion Resistance Good Chemical Resistance Good Creep Resistance Good Dimensional Stability Good Electrical Properties Good Processability Good Strength Good Thermal Stability Good Weather Resistance High Hardness High Stiffness Low Moisture Absorption Low to No Water Absorption
Uses	Automotive Applications Fuel Lines Thin-walled Parts Wire & Cable Applications
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.26	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (250°C/2.16 kg)	12.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Across Flow	1.4	%
Flow	1.4	%
Water Absorption (Saturation, 23°C)	0.35	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	65		ISO 868
Ball Indentation Hardness ¹	50.0	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	550	MPa	ISO 527-2
Tensile Stress (Yield)	27.0	MPa	ISO 527-2/50
Tensile Strain			ISO 527-2/50
Yield	23	%
Break	> 50	%

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C, Complete Break	8.0	kJ/m²
23°C, Complete Break	30	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C, Complete Break	No Break
23°C, Complete Break	No Break

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	110	°C	ISO 75-2/B
1.8 MPa, Unannealed	50.0	°C	ISO 75-2/A
Vicat Softening Temperature
--	190	°C	ISO 306/A
--	125	°C	ISO 306/B
Melting Temperature	200 to 205	°C	ISO 11357-3
CLTE			ISO 11359-2
Flow : 23 to 55°C	1.5E-4	cm/cm/°C
Transverse : 23 to 55°C	1.5E-4	cm/cm/°C

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+13	ohms	IEC 60093
Volume Resistivity (23°C)	1.0E+15	ohms·cm	IEC 60093
Electric Strength ²(1.00 mm, in Oil)	27	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
23°C, 100 Hz	4.00
23°C, 1 MHz	3.60
Dissipation Factor			IEC 60250
23°C, 100 Hz	0.022
23°C, 1 MHz	0.033
Comparative Tracking Index			IEC 60112
-- ³	575	V
Solution A	600	V

Flammability	Nominal Value	Unit	Test Method
Flammability Classification			IEC 60695-11-10, -20
0.800 mm	HB
1.60 mm	HB
Glow Wire Flammability Index (2.00 mm)	750	°C	IEC 60695-2-12
Glow Wire Ignition Temperature (2.00 mm)	750	°C	IEC 60695-2-13

Additional Information	Nominal Value		Test Method
Electrolytical Corrosion	A1 step		IEC 60426

Note Message
1 .	H 30
2 .	K 20/P 50
3 .	100 Drops value

Resin Grade	Manufacturer	Category	Trademark
ALTECH® NXT PP-H A 2430/450 GF20 MR10 CP	ALBIS PLASTIC GmbH	PP Homopolymer	ALTECH® NXT PP-H
DOWLEX™ NG 2432.10 UE	The Dow Chemical Company	LLDPE	DOWLEX™
IROGRAN® A 85 P 4350	Huntsman Corporation	TPU-Polyether	IROGRAN®
Jackdaw ABS GX10BL6576	Jackdaw Polymers	ABS	Jackdaw ABS
ESTOPLAST XU 150BB10	Ester Industries Ltd.	Nylon 6	ESTOPLAST XU