Tenopom® POM A3 MF TZ NTLA010 PR308
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Tenopom® POM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fgnKcO_Tenopom-POM-A3-MF-TZ-NTLA010-PR308.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyacetal homopolymer, impact modified (Tough), medium viscosity, easy processing. Indicated for injection. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/1.05 kg) | 5.0 to 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.2 to 1.7 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 51.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 73 | % | ASTM D638 |
| Flexural Modulus | 2230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 155 | °C | |
| 1.8 MPa, Unannealed | 77.0 | °C | |
| Peak Melting Temperature | 177 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+14 | ohms·cm | ASTM D257 |
| Dissipation Factor (1 MHz) | 5.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 210 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PP F008F | Braskem America Inc. | PP Homopolymer | Braskem PP |
| Carbotex KV-75FD | Kotec Corporation | PC | Carbotex |
| Pujie CPE-135C | Zhanhua Pujie Chemical Technology Co.,Ltd | CPE | Pujie |
| Sylvin 86032-90 Clear 8443 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VALOX™ 830 resin | SABIC Innovative Plastics | PBT | VALOX™ |