TECHNYL® A 230 V13 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fgH6s0_TECHNYL-A-230-V13-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified polyamide 66, reinforced with 13% of glass fibre, with improved impact resistance, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.19 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.85 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.75 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.850 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5500 | 3650 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield | 100 | 60.0 | MPa | |
| Break | 100 | 600 | MPa | |
| Tensile Strain (Break) | 4.0 | 6.0 | % | ISO 527-2/1A |
| Flexural Modulus | 4200 | 2500 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 65 | 60 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 8.0 | 10 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 225 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 5.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 35 | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.50 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.010 | 0.050 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | 600 | V | |
| Solution B | 525 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® Fine Powders D40 NATURAL | Arkema | Nylon 11 | Rilsan® Fine Powders |
| Quadrant EPP ERTALON® 6 XAU+ | Quadrant Engineering Plastic Products | Nylon 6 | Quadrant EPP |
| Sindustris PC GN1007FM | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| HANWHA EVA X1629 | Hanwha Chemical | EVA | HANWHA EVA |
| WELLAMID Nylon 6000 GV 30 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |