Zenite® 6330
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Zenite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fgCAay_Zenite-6330.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Zenite® 6330 is a 30% mineral reinforced liquid crystal polymer for injection molding. It has excellent impact resistance, excellent heat deflection temperature and and is well suited for all kinds of demanding applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.64 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.65 | % | |
| Flow | 0.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 9500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 60 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 275 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 245 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 120 | °C | ISO 11357-2 |
| Melting Temperature 2 | 335 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 8.0E-6 | cm/cm/°C | |
| Transverse | 4.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.80 | ||
| 1 MHz | 3.40 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.014 | ||
| 1 MHz | 0.031 | ||
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.850 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| Oxygen Index | 47 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Processing (Melt) Temp | 350 to 360 | °C | |
| Mold Temperature | 40.0 to 150 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4000 TFE 20 | RTP Company | PPA | RTP |
| Sanren N110 (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| ABSCOM® T4060 | Polymer Compounders Limited | ABS | ABSCOM® |
| HiPrene® M560ST | GS Caltex | PP Impact Copolymer | HiPrene® |
| SQUARE® LSG6933-10A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |