PULSE™ EXT 200
| Category: | PC+ABS , PC/ABS Engineering Resin |
| Manufacturer: | Trinseo |
| Trademark: | PULSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fgBaB5_PULSE-EXT-200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Heat, High Impact PC/ABS resin for injection molded automotive plating and painting trim applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.5 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 47.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 180 | % | ASTM D638 |
| Flexural Modulus | 2180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -29°C | 49 | kJ/m² | |
| 23°C | 44 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| -34°C | 510 | J/m | |
| 23°C | 600 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 116 | °C | |
| 1.8 MPa, Unannealed | 93.3 | °C | |
| Vicat Softening Temperature | 111 | °C | ASTM D1525 3 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® D black | Röchling Engineering Plastics SE & Co. KG | HMWPE | POLYSTONE® |
| Wellamid® GF20-60 XE-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Flontech® FT-1-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Kynar® 761 | Arkema | PVDF | Kynar® |
| Karina WHITE PVC COMPOUND 802-10/93-AY-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |