EMERGE™ ABS 5302
| Category: | ABS , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fd910l_EMERGE-ABS-5302.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE ABS 5302 is a black, 20% glass filled ABS which is suitable for use in a wide variety of internal structural component applications in the Information Technology market. This resin exhibits a property balance of flow, rigidity, and dimensional stability. Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 5.0 | g/10 min | |
| 230°C/3.8 kg | 1.6 | g/10 min | |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.15 to 0.25 | % | |
| Across Flow | 0.35 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 70.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 70.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 2.0 | % | |
| Break, 3.20 mm, Injection Molded | 2.0 | % | |
| Flexural Modulus (3.20 mm, Injection Molded) | 6350 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 72 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 105 | °C | |
| 1.8 MPa, Unannealed | 100 | °C | |
| Vicat Softening Temperature | |||
| -- | 106 | °C | ASTM D1525 1 |
| -- | 115 | °C | ASTM D1525 2 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 29°C | 9.0E-5 | cm/cm/°C | |
| Transverse : -30 to 29°C | 9.4E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 3(1.00 mm, BK, NC, GY) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| 2 . | Rate B (120°C/h), Loading 1 (10 N) |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mowital® B 60 H | Kuraray Co., Ltd. | PVB | Mowital® |
| HiFill® PP TM20 FR-2 | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| Hostaform® S 9243 XAP² ™ LS | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Huafon HF-3390AX | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Sylvin 5210-75 Orange 5110 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |