ESTAPROP HK 4000 CH-HT
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Cossa Polimeri S.r.l. |
| Trademark: | ESTAPROP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fd7lD0_ESTAPROP-HK-4000-CH-HT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ESTAPROP HK 4000 CH-HT is a Polypropylene Copolymer (PP Copolymer) product. It can be processed by injection molding and is available in Europe. Typical application: Automotive. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.890 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 55 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 to 2.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 45 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ageing Test | > 700.0 | hr | Internal Method |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 6594B-G88E | TSRC Corporation | SEBS | T-Blend® |
| VITAMIDE® AY24BK6722 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Duron PPE/PA 820 | ProPolymers Inc. | Nylon+PPE | Duron |
| Kumho ABS 720R | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| Latilub 30/R-07 GRT | LATI S.p.A. | PS (GPPS) | Latilub |