POLIGOM G/30 BIANCO
| Category: | EPDM , Ethylene Propylene Diene Terpolymer |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | POLIGOM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fc8kUu_POLIGOM-G-30-BIANCO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLIGOM G/30 : is the trade-mark of our crosslinkable halogen free EPR/EPDM. POLIGOM G/30 BIANCO : is a chemically crosslinkable rubber for low voltage cable insulation and sheathing. It is a conveniently grafted compound able to react in presence of moisture and of a catalyst MAC/202 or MAC/308 PSF. These two compounds, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 95/5 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 1.0 - 5.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 12.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 800 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (150°C, 168 hr) | 8.0 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air (150°C, 168 hr) | -17 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811 | ||
| 250°C | 60 | % | IEC 60811 |
| Residual : 250°C | 10 | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Conductivity | kJ/m² | IEC 60754-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | 0 | ppm | IEC 60754-1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 210 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Additional Information |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by:-Immersion of the bobbin in hot water at 85/90 °C f or two hours (up to 1/1,5 mm thickness)-Steam treatment at 0,15 bar for 5/6 hours.-Ambient crosslink is possible on sufficient time that depend from air temperature and relative moisture. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 | °C | |
| Cylinder Zone 2 Temp. | 175 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 205 | °C | |
| Die Temperature | 215 | °C |
| Note Message | |
|---|---|
| 1 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 5061 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Braskem PP RP 347 | Braskem | PP Random Copolymer | Braskem PP |
| K-Prene SHEATHING EPR 5064 | Technovinyl Polymers India Ltd. | MPR | K-Prene |
| Hifax TYC 258X NA BLACK | LyondellBasell Industries | PP, Unspecified | Hifax |
| LNP™ THERMOCOMP™ WB006 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |