Stanyl® Diablo OCD2300 BLK
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | famskp_Stanyl-Diablo-OCD2300-BLK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stanyl® Diablo OCD2300 BLK is a Polyamide 46 (Nylon 46) material filled with 50% glass fiber. It is available in Europe. Primary attribute of Stanyl® Diablo OCD2300 BLK: Heat Stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.62 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 17000 | 8000 | MPa | |
| 120°C | 6900 | -- | MPa | |
| 160°C | 6100 | -- | MPa | |
| 180°C | 5600 | -- | MPa | |
| 200°C | 4500 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Break | 240 | 135 | MPa | |
| Break, 120°C | 110 | -- | MPa | |
| Break, 160°C | 90.0 | -- | MPa | |
| Break, 180°C | 75.0 | -- | MPa | |
| Break, 200°C | 60.0 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break | 2.4 | 6.3 | % | |
| Break, 120°C | 7.5 | -- | % | |
| Break, 160°C | 8.5 | -- | % | |
| Break, 180°C | 9.0 | -- | % | |
| Break, 200°C | 9.5 | -- | % | |
| Flexural Modulus | ISO 178 | |||
| -- | 17000 | 8000 | MPa | |
| 120°C | 6900 | -- | MPa | |
| 160°C | 6100 | -- | MPa | |
| 180°C | 5600 | -- | MPa | |
| 200°C | 4500 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 14 | 14 | kJ/m² | |
| 23°C | 17 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 95 | kJ/m² | |
| 23°C | 95 | 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 1 | 282 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 4.0E-5 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 295 to 305 | °C | |
| Nozzle Temperature | 280 to 300 | °C | |
| Processing (Melt) Temp | 295 to 305 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinelec CCB2765/G | Teknor Apex Asia Pacific PTE. LTD. | PS (Specialty) | Sinelec |
| TRYCITE™ 1003U | The Dow Chemical Company | PS (GPPS) | TRYCITE™ |
| Abstron SE45I | Bhansali Engineering Polymers Limited | ABS | Abstron |
| DESLON™ 6 DSC121HI | DESCO Co., Ltd. | Nylon 6 | DESLON™ 6 |
| Kangxi® ABS-20GF | Wuxi Kangxi Plastics Technology Co.,Ltd. | ABS | Kangxi® |