Duratron® T5530

Category:	PAI , Polyamide-imide
Manufacturer:	Quadrant Engineering Plastic Products
Trademark:	Duratron®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	fafIoH_Duratron-T5530.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Duratron® T5530 is 30% glass reinforced, compression molded PAI. It is ideal for higher load structural or electronic applications. This grade is similar in composition to Duratron® T5030 PAI. It is selected for larger shapes or when the greatest degree of dimensional control is required.

Duratron® PLA is the highest performing melt processable plastic. It has superior resistance to elevated temperatures. It is capable of performing under severe stress conditions at continuous temperatures to 500°F (260°C). Parts machined from Duratron® PLA stock shapes provide greater compressive strength and higher impact resistance than most advanced engineering plastics. Its extremely low coefficient of linear thermal expansion and high creep resistance deliver excellent dimensional stability over its entire use range. Duratron® PLA is an amorphous material with a Tg (glass transition temperature) of 537°F (280°C).

Data provided by Quadrant Engineering Plastic Products from tests on stock shapes and parts produced by Quadrant EPP.

General Information
Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Features	Acid Resistant Alcohol Resistant Amorphous Good Chemical Resistance Good Compressive Strength Good Creep Resistance Good Dimensional Stability Good Stiffness Good Thermal Stability Good Wear Resistance High Impact Resistance High Strength Hydrocarbon Resistant Solvent Resistant
Uses	Electrical/Electronic Applications Structural Parts
Forms	Customizable Forms Disc Preformed Parts Rod Sheet Tubing
Processing Method	Compression Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.61	g/cm³	ASTM D792
Water Absorption			ASTM D570
24 hr	0.30	%
Saturation	1.5	%

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness			ASTM D785
E-Scale	85
M-Scale	125
Durometer Hardness (Shore D)	90		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	6210	MPa	ASTM D638
Tensile Strength (Ultimate)	103	MPa	ASTM D638
Tensile Elongation (Break)	3.0	%	ASTM D638
Flexural Modulus	6210	MPa	ASTM D790
Flexural Strength (Yield)	138	MPa	ASTM D790
Compressive Modulus	4140	MPa	ASTM D695
Compressive Strength (10% Strain)	186	MPa	ASTM D695
Coefficient of Friction (vs. Steel - Static)	0.20		Internal Method

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	37	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	271	°C	ASTM D648
Maximum Use Temperature - Long Term, Air	260	°C

Additional Information	Nominal Value	Unit	Test Method
Limiting Pressure Velocity ¹	0.701	MPa·m/s	Internal Method

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	275	°C	ASTM D3418
CLTE - Flow ²(-40 to 149°C)	4.7E-5	cm/cm/°C	ASTM E831
Thermal Conductivity	0.36	W/m/K	ASTM F433

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity ³	> 1.0E+13	ohms	Internal Method
Dielectric Strength ⁴	28	kV/mm	ASTM D149
Dielectric Constant (1 MHz)	6.30		ASTM D150
Dissipation Factor (1 MHz)	0.050		ASTM D150

Flammability	Nominal Value	Unit	Test Method
Flame Rating (3.18 mm, Estimated Rating)	V-0		UL 94

Note Message
1 .	4:1 safety factor
2 .	68°F
3 .	EOS/ESD S11.11
4 .	Method A (Short-Time)

Resin Grade	Manufacturer	Category	Trademark
SEQUEL® 1718	LyondellBasell Industries	TPO (POE)	SEQUEL®
Tygothane C-210-A	Saint Gobain - Norton	PUR-Ester	Tygothane
UNIPA® lm	Nytef Plastics, Ltd.	Nylon 612	UNIPA®
Hanwha Total PP FB52	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, Unspecified	Hanwha Total PP
ImerPlast™ 20	Imerys Minerals	Polyolefin, Unspecified	ImerPlast™