LNP™ THERMOCOMP™ DF004P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fZxhmv_LNP-THERMOCOMP-DF004P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* DF004P is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Exceptional Processing. Also known as: LNP* THERMOCOMP* Compound DF-1004 EP Product reorder name: DF004P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.67 | % | ISO 294-4 |
| Flow : 24 hr | 0.23 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.12 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.19 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6200 | MPa | ASTM D638 |
| -- | 6050 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 104 | MPa | ASTM D638 |
| Break | 102 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 3.2 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 6170 | MPa | ASTM D790 |
| -- | 5990 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 173 | MPa | ASTM D790 |
| -- | 163 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C 2 | 9.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 710 | J/m | ASTM D4812 |
| 23°C 3 | 48 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.85 | J | ASTM D3763 |
| -- | 2.36 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 139 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 3.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.4E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 6.9E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yuyao PBT 3060G20 | Yuyao Tenglong Plastics Co., Ltd. | PBT | Yuyao PBT |
| LEXAN™ LUX9132C resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ THERMOCOMP™ NF004 compound | SABIC Innovative Plastics | PC+ABS | LNP™ THERMOCOMP™ |
| POCAN® DP C 1502 000000 | LANXESS Asia/Pacific | PC+PBT | POCAN® |
| LNP™ LUBRICOMP™ RAL23S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |