XAREC™ SP130
| Category: | SPS , Syndiotactic Polystyrene |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | XAREC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fZpxP8_XAREC-SP130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XAREC™ SP130 is a Syndiotactic Polystyrene (SPS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 80°C | 0.40 to 1.2 | % | |
| Flow : 80°C | 0.40 to 1.4 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.4 | % | ISO 527-2 |
| Flexural Modulus | 3000 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 41 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 4.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 29 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed 2 | 120 | °C | ISO 75-2/B |
| 0.45 MPa, Unannealed 3 | 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed 4 | 100 | °C | ISO 75-2/A |
| 1.8 MPa, Unannealed 5 | 95.0 | °C | ISO 75-2/A |
| CLTE | TMA | ||
| Flow : -30 to 30°C | 7.7E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.3E-5 | cm/cm/°C | |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 70 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | < 1.0E-3 | IEC 60250 | |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) 6 | PLC 0 | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (> 1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 24h |
| 2 . | Mold temperature: 150°C |
| 3 . | Mold temperature: 80°C |
| 4 . | Mold temperature: 150°C |
| 5 . | Mold temperature: 80°C |
| 6 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 9110 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Sofprene T® 550100A75 | SO.F.TER. SPA | SBS | Sofprene T® |
| VECTOR® 2518A | Dexco Polymers LP | SBS | VECTOR® |
| LNP™ THERMOCOMP™ WX15003 compound | SABIC Innovative Plastics Europe | PBT | LNP™ THERMOCOMP™ |
| GELOY™ XP7550 resin | SABIC Innovative Plastics | ASA+PC | GELOY™ |