Slique™ 1850W61 Bk-1
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Technical Polymers, LLC |
| Trademark: | Slique™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fZOGrN_Slique-1850W61-Bk-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA6, 40% Glass Reinforced, Friction/Wear Modified, Black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 138 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 1.0 - 3.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 11700 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 228 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C | 4.2 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 213 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 204 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.9 - 79.4 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 - 288 | °C | |
| Mold Temperature | 65.6 - 98.9 | °C |
| Injection instructions |
|---|
| Can be over-dried. Do not exceed 180 - 200 F for more than 3 hours. Typical drying time assumes unopened packaging and utilization of a dehumidifying dryer with a dewpoint of -40° and appropriate airflow. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siloxane Masterbatch MB50-008 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| SLOVALEN® PH 69 GF 25 | Plastcom | PP, Unspecified | SLOVALEN® |
| HI-ZEX™ 1608J | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| PEXLOY™ PXPG10-BK10 | Pier One Polymers, Inc. | PC+Polyester | PEXLOY™ |
| Plexiglas® Satinice df23 7N | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |