KumhoSunny PA/ABS HNB0270
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PA/ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fZEYUy_KumhoSunny-PA-ABS-HNB0270.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HNB 0270 has the feature of high impact. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 240°C/10.0 kg | 25 to 45 | g/10 min | ASTM D1238 |
| 240°C/10.0 kg | 50 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.60 to 0.80 | % | ASTM D955 |
| -- | 0.60 to 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 45.0 | MPa | ASTM D638 |
| -- | 40.0 | MPa | ISO 527-2/50 |
| Tensile Elongation (Break) | > 50 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 1800 | MPa | ASTM D790 |
| -- 1 | 1750 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 60.0 | MPa | ASTM D790 |
| -- 2 | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179 | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Notched Izod Impact | |||
| 3.20 mm | 700 | J/m | ASTM D256 |
| 23°C 4 | 60 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 105 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 108 | °C | ASTM D1525 6 |
| -- | 105 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 210 to 230 | °C | |
| Nozzle Temperature | 220 to 240 | °C | |
| Processing (Melt) Temp | 220 to 230 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 4J |
| 4 . | 5.5J |
| 5 . | 120°C/h |
| 6 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2404H4 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| ASACOM™ S9500-10 | Polymer Compounders Limited | ASA | ASACOM™ |
| KPOL-LDPE LD K-0.30/921 | KPOL Chem Co. | LDPE | KPOL-LDPE |
| LEXAN™ PC2200 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Vipel® K022-ACT-30 | AOC, L.L.C. | Vinyl Ester | Vipel® |