VESTAKEEP® Film 0FH81
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAKEEP® Film |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fXzAFR_VESTAKEEP-Film-0FH81.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VESTAKEEP® film 0FH81 is a cast film based on 100% unreinforced polyether ether ketone (PEEK). The film is amorphous. VESTAKEEP® film 0FH81 is designed for thermoforming thin walled parts from the melt. The material features the lowest extrusion related internal stresses possible. Applications of the film are cutting edge precision parts made by thermoforming, e.g.:
The low internal stresses of the film allow for walls of lowest thickness tolerance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.26 | g/cm³ | ISO 1183 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3/100 | ||
| Yield | 60.0 | MPa | |
| -- | 120 | MPa | |
| Tensile Elongation (Break) | > 150 | % | ISO 527-3/100 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | 150 | °C | |
| Crystallization Point - Cold | > 165 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistance | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistance | 1.0E+14 | ohms | IEC 60093 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Breakdown Voltage | EN 60243-1 | ||
| 75.0 µm | 13500 | V | |
| 125.0 µm | 17500 | V |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 0.0750 mm | 190 | kV/mm | |
| 0.125 mm | 140 | kV/mm | |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.80 | ||
| 1 kHz | 2.90 | ||
| 1 MHz | 2.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 1 kHz | 3.0E-3 | ||
| 1 MHz | 5.0E-3 | ||
| Comparative Tracking Index | IEC 60112 | ||
| -- | 200 | V | |
| Solution A 2 | 175 | V |
| Note Message | |
|---|---|
| 1 . | 2nd Heating |
| 2 . | 100 drops value |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 10.2.0 | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |
| Verolloy A5626 | PlastxWorld Inc. | ABS+Nylon | Verolloy |
| Five Plus™ HPP20T | Noble Polymers | PP Homopolymer | Five Plus™ |
| LEXAN™ 131P resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ STAT-KON™ MD000ISC compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |