Vydyne® 909 Datasheet,Nylon 66/6,Ascend Performance Materials Operations LLC-SHANGHAI SUSHENG

Message
Vydyne 909 is an halogenated, 25% glass-filled, flame-retardant PA66/6 copolymer with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has an Underwriters Laboratories UL 94 flammability classification of V-0 at 0.4 mm (0.016") thick.

General Information
Filler / Reinforcement	Glass Fiber, 25% Filler by Weight
Additive	Halogen Lubricant
Features	Flame Retardant Good Crack Resistance Good Mold Release Good Toughness Halogenated High Rigidity High Strength Ignition Resistant Lubricated
Uses	Appliances Automotive Electronics Bobbins Connectors Electrical Housing Electrical Parts Electrical/Electronic Applications Fasteners Industrial Applications Lighting Applications Living Hinges Printed Circuit Boards Switches
RoHS Compliance	RoHS Compliant
UL File Number	E70062
Appearance	Natural Color
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.47	--	g/cm³	ISO 1183
Molding Shrinkage				ISO 294-4
Across Flow : 23°C, 2.00 mm	1.0	--	%
Flow : 23°C, 2.00 mm	0.40	--	%
Water Absorption				ISO 62
23°C, 24 hr	0.70	--	%
Equilibrium, 23°C, 50% RH	1.3	--	%

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	9100	7100	MPa	ISO 527-2
Tensile Stress (Break, 23°C)	132	90.0	MPa	ISO 527-2
Tensile Strain (Break, 23°C)	2.2	3.0	%	ISO 527-2
Flexural Modulus (23°C)	8300	5000	MPa	ISO 178
Flexural Strength (23°C)	193	140	MPa	ISO 178
Poisson's Ratio	0.40	--		ISO 527-2

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	9.5	--	kJ/m²
23°C	9.4	--	kJ/m²
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	35	--	kJ/m²
23°C	40	--	kJ/m²
Notched Izod Impact Strength (23°C)	9.0	--	kJ/m²	ISO 180

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	250	--	°C	ISO 75-2/B
1.8 MPa, Unannealed	230	--	°C	ISO 75-2/A
Melting Temperature	250	--	°C	ISO 11357-3
CLTE				ISO 11359-2
Flow : 23 to 55°C, 2.00 mm	2.0E-5	--	cm/cm/°C
Transverse : 23 to 55°C, 2.00 mm	1.0E-4	--	cm/cm/°C
RTI Elec				UL 746
0.400 mm	65.0	--	°C
0.750 mm	130	--	°C
1.50 mm	130	--	°C
3.00 mm	130	--	°C
RTI Imp				UL 746
0.400 mm	65.0	--	°C
0.750 mm	65.0	--	°C
1.50 mm	95.0	--	°C
3.00 mm	95.0	--	°C
RTI Str				UL 746
0.400 mm	65.0	--	°C
0.750 mm	110	--	°C
1.50 mm	110	--	°C
3.00 mm	110	--	°C

Electrical	Dry	Conditioned	Unit	Test Method
Arc Resistance (3.00 mm)	PLC 6	--		ASTM D495
Comparative Tracking Index (3.00 mm)	250 to 399	--	V	IEC 60112
High Amp Arc Ignition (HAI)				UL 746
0.750 mm	PLC 0	--
1.50 mm	PLC 0	--
High Voltage Arc Tracking Rate (HVTR) (3.00 mm)	PLC 3	--		UL 746
Hot-wire Ignition (HWI)				UL 746
0.750 mm	PLC 0	--
1.50 mm	PLC 0	--

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
0.400 mm	V-0	--
0.750 mm	V-0	--
1.50 mm	V-0	--
3.00 mm	V-0	--
Glow Wire Flammability Index				IEC 60695-2-12
0.400 mm	960	--	°C
0.750 mm	960	--	°C
1.50 mm	960	--	°C
3.00 mm	960	--	°C
Glow Wire Ignition Temperature				IEC 60695-2-13
0.400 mm	930	--	°C
0.750 mm	750	--	°C
1.50 mm	750	--	°C
3.00 mm	800	--	°C
Oxygen Index	32	--	%	ISO 4589-2

Category:	Nylon 66/6 , Polyamide 66/6 Copolymer
Manufacturer:	Ascend Performance Materials Operations LLC
Trademark:	Vydyne®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	fXdOL5_Vydyne-909.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Sumitomo DAP 73-70-70 V0-P	Sumitomo Bakelite North America, Inc.	DAP	Sumitomo DAP
Fluoroloy® A08	Saint Gobain Performance Plastics	TP, Unspecified	Fluoroloy®
JSR EPR EP22	JSR Corporation	EPDM	JSR EPR
LNP™ THERMOCOMP™ PF00ASXS compound	SABIC Innovative Plastics	Nylon 6	LNP™ THERMOCOMP™
Durethan® BKV 30 G W1 901317	LANXESS Asia/Pacific	Nylon 6	Durethan®