Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
Manufacturer: | INEOS Olefins & Polymers Europe |
Trademark: | Eltex® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | fX99AA_Eltex-EXP9415.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Eltex® EXP9415 is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties:
Applications Eltex® EXP9415 has been developed for use in collation shrinkwrap, food packaging and other thin film applications where excellent balance between film strength and rigidity is required together with good optical properties. In addition, Eltex® EXP9415 offers easy extrudability We recommend that you consult your INEOS technical representative for further advice on the use of Eltex® EXP9415 |
General Information | |
---|---|
Additive |
|
Features |
|
Uses |
|
RoHS Compliance |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density 1 | 0.927 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) | 1.3 | g/10 min | ISO 1133 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Coefficient of Friction | < 0.30 | ASTM D1894 |
Films | Nominal Value | Unit | Test Method |
---|---|---|---|
Film Thickness - Tested | 25 | µm | |
Tensile Modulus | ISO 1184 | ||
1% Secant, MD : 25 µm | 230 | MPa | |
1% Secant, TD : 25 µm | 270 | MPa | |
Tensile Stress | ISO 1184 | ||
MD : Yield, 25 µm | 13.0 | MPa | |
TD : Yield, 25 µm | 13.0 | MPa | |
MD : Break, 25 µm | 55.0 | MPa | |
TD : Break, 25 µm | 50.0 | MPa | |
Tensile Elongation | ISO 1184 | ||
MD : Break, 25 µm | 570 | % | |
TD : Break, 25 µm | 690 | % | |
Dart Drop Impact (25 µm) | 200 | g | ASTM D1709A |
Elmendorf Tear Strength | ASTM D1922 | ||
MD : 25 µm | 160 | g | |
TD : 25 µm | 560 | g |
Optical | Nominal Value | Unit | Test Method |
---|---|---|---|
Gloss (45°, 25.0 µm) | 65 | ASTM D2457 | |
Haze (25.0 µm) | 7.0 | % | ASTM D1003 |
Extrusion | Nominal Value | Unit | |
---|---|---|---|
Melt Temperature | 190 to 230 | °C |
Note Message | |
---|---|
1 . | Conditioning ISO 1872/1 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
RTP 1405 HF TFE 5 | RTP Company | PESU | RTP |
TOTAL Polyethylene MDPE LF 38 YSCF | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
APEX® RS 9118 UV | Teknor Apex Company | PVC, Rigid | APEX® |
Elastron® D D101.A90.N | Elastron USA, Inc. | SBS | Elastron® D |
Karina WHITE PVC COMPOUND 851-10/127-Y-ERYB-AS-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |