INEOS HDPE K44-15-122
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fWxnhE_INEOS-HDPE-K44-15-122.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| K44-15-122 is a natural high-density polyethylene copolymer designed specifically for extrusion of pipe. It has NSF Standard 14 certification for potable water applications, complies with ANSI/NSF Standard 61 health effects requirements, and is recognized by the Plastic Pipe Institute as having a pipe material designation code of PE 3608 (formerly PE 3408). A pressure rated formulation is also produced when this product is extruded in combination with an INEOS-approved black masterbatch. The resulting formulation known as K44-15-123 has NSF Standard 14 certification and complies with ANSI/NSF Standard 61 health effects requirements, is certified to CSA Standard B137.1-05 and B137.4-05, and is listed with the Plastic Pipe Institute as having a PE 3608 (formerly PE3408) and PE80 pipe material designation code. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.944 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 12 | g/10 min | |
| 190°C/5.0 kg | 0.52 | g/10 min | |
| Environmental Stress-Cracking Resistance (100% Igepal, F50) | > 1000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 20.7 | MPa | |
| Break | 34.5 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 11 | % | |
| Break | > 800 | % | |
| Flexural Modulus - 2% Secant | 752 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 480 | J/m | ASTM D256 |
| Notched Izod Impact (Area) | 45.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -118 | °C | ASTM D746 |
| Vicat Softening Temperature | 121 | °C | ASTM D1525 |
| Oxidation Induction Time (210°C) | > 35 | min | ASTM D3895 |
| Thermal Stability | 127 | °C | ASTM D3350 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cell Classification | 335464A | ASTM D3350 | |
| PENT - Notch Tensile | > 100 | hr | ASTM F1473 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx CPP5B10 | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| Zythane® 6080A | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| CERTENE™ HI-2053 | Muehlstein | HDPE | CERTENE™ |
| OPTODYNE™ UV-1000 | Daikin Fluorochemicals (China) Co., Ltd. | Epoxy | OPTODYNE™ |
| LNP™ THERMOCOMP™ NF001 compound | SABIC Innovative Plastics | PC+ABS | LNP™ THERMOCOMP™ |