SABIC® Vestolen A BI5828
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® Vestolen A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fW41II_SABIC-Vestolen-A-BI5828.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® Vestolen A BI5828 is a bimodal HDPE that combines high ESCR and stiffness with good impact resistance. It is typically used for blow moulding of consumer packaging up to 5 l. This grade is typically used for packaging the majority of detergents, cleaners, shampoos and cosmetics. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 28 | g/10 min | |
| 190°C/5.0 kg | 1.2 | g/10 min | |
| Environmental Stress-Cracking Resistance (2.00 mm, 10% Igepal CO-630, Compression Molded, F50) | 300 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1300 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 28.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 36.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 1000 | % | ISO 527-2/1BA/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Compression Molded | 7.0 | kJ/m² | |
| 23°C, Compression Molded | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 79.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 127 | °C | ISO 306/A |
| Melting Temperature (DSC) | 135 | °C | ISO 11357-3 |
| Enthalpy Change | 200 | J/g | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 127 MF | RTP Company | PP Homopolymer | RTP |
| Moplen HP480S | PolyMirae | PP Homopolymer | Moplen |
| Mowiol® 4-98 low ash | Kuraray Co., Ltd. | PVOH | Mowiol® |
| Plexiglas® Satinice df33 zk6BR | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| Hyflon® PFA P130X | Solvay Specialty Polymers | PFA | Hyflon® PFA |