Plexiglas® Heatstop 8N black

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Industries AG
Trademark:	Plexiglas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	fVwIAT_Plexiglas-Heatstop-8N-black.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Product Profile:
PLEXIGLAS® Heatstop 8N black is an amorphous
thermoplastic molding compound (PMMA).

Typical properties of PLEXIGLAS® molding compounds are:

good flow

high mechanical strength, surface hardness and abrasion resistance

very good weather resistance

Special properties of PLEXIGLAS® Heatstop 8N black are:

heat-reflection (IR)

high total solar reflection (TSR), reflects 21% of the solar energy

reduces the heat build-up of plastic parts, thus increases the dimension stability.

Application:
PLEXIGLAS® Heatstop 8N black is suitable for injection molding of technical components, as well as for extrusion/coextrusion. Owing to its superior brilliance, high-gloss (Class A) black surfaces can be obtained.

Examples:
black automotive add-on parts like spoiler, pillar and roof trims, black automotive parts like roof modules.

General Information
Features	Good Abrasion Resistance Good Flow Good Weather Resistance High Gloss High Hardness High Strength
Uses	Automotive Applications Automotive Exterior Parts Automotive Exterior Trim
Appearance	Black
Forms	Pellets
Processing Method	Coextrusion Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	3.00	cm³/10min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3300	MPa	ISO 527-2/1
Tensile Stress (Break)	77.0	MPa	ISO 527-2/5
Tensile Strain (Break)	5.5	%	ISO 527-2/5

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	20	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	103	°C	ISO 75-2/B
1.8 MPa, Unannealed	98.0	°C	ISO 75-2/A
Glass Transition Temperature	117	°C	ISO 11357-2
Vicat Softening Temperature	108	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	8.0E-5	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94
Fire Rating	B2		DIN 4102

Injection	Nominal Value	Unit
Drying Temperature	< 98.0	°C
Drying Time	2.0 to 3.0	hr
Processing (Melt) Temp	220 to 260	°C
Mold Temperature	60.0 to 90.0	°C

Resin Grade	Manufacturer	Category	Trademark
Sarlink® TPV 24580	Teknor Apex Company	TPV	Sarlink® TPV
TEREZ PA 6 7500 TF 15	TER HELL PLASTIC GMBH	Nylon 6	TEREZ PA 6
Andur M-80 AS/Curative	Anderson Development Company	PUR-MDI	Andur
Karina BLUE PVC COMPOUND 900D06/469-AT-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
RTP 2099 X 90635	RTP Company	PC+PBT	RTP